Home Advanced Ceramics Zirconia Lifting Cup
Lifting Cup

Lifting Cup

  • Product Description

    Our medical zirconia lifting-cups provide customizable solutions with proven biocompatibility, optimal wear resistance, and autoclave compatibility. The precision-engineered surface finish ensures minimal tissue interaction, with adjustable parameters for size and geometry to accommodate various clinical applications.

  • Product Properties

    High Hardness
    Good Chemical Stability
    Good Biocompatibility
    Corrosion Resistance
    Technical Support

Technical support

Customize the product according to your usage

We would like to improve your product design, improve performance and reduce costs to suit your needs

Enhancement of after-sales services for product applications

  Alumina Zirconia Yttria Aluminum Nitride Silicon Nitride Silicon Carbide
Item (JFM) Unit JC-AZ025A JC-A995A JC-A990A JC-A995A JC-A997A JC-A997B JC-A999A JC-Z08 JC-ZA20 JC-Y100A JC-AN100A JC-AN180 JC-SN-GPS-01 JC-SN-GPS-02 JC-SC101
Physical Property  
Content % - 95.0% 99.0% 99.5% 99.7% 99.7% 99.9% - - - - - - - -
Colour   Milky White White White Milky White Milky White Milky White White Milky White Milky White Greyish White Milky White Greyish White Greyish White Greyish White Black
Density g/cm3 4.4 3.7 3.8 3.9 3.92 3.94 3.95 6.0 5.6 4.9 3.2 3.3 3.21 3.23 3.15
Mechanical Behavior  
Vickers Hardness GPa 15 13.7 15.2 16.0 17.2 17.2 17.5 12.5 10.5 6 11.2 10.5 13.5 14.8 23
Bending Strength Mpa 650 350 310 360 380 380 400 1000 750 130 220 320 720 900 500
Compressive Strength Mpa - - 2160 2350 2380 2400 2560 2100 2300 3000 450 - 3200 3200 3900
Young's Modulus GPa 320 320 360 370 380 380 380 200 200 160 310 320 300 310 420
Poisson's Ratio / 0.25 0.23 0.23 0.23 0.23 0.23 0.23 0.31 0.31 - 0.24 0.24 0.28 - 0.17
Fracture Toughness Mpa.m1/2 5 3-4 3-4 4 4.8 5 5.4 4.6 7.4 1.1 3.2 3.3 6.5 7 3.2
Thermal Property    
Coefficient of Thermal Expansion 10-6/°C 9 7.2 7.2 7.2 7.2 7.2 7.2 10.5 10 7.2 4.6 4.6 2.8 2.8 4.3
Thermal Conductivity W/(m.K) 19 24 29 32 32 32 34 3 3 14 120 180 26 28 160
Specific Heat Capacity J/(g.K) - 0.78 0.79 0.78 0.79 0.79 0.78 0.46 0.46 0.45 0.72 0.72 0.64 0.64 0.67
Maximum Operating Temperature °C 1600 1500 1600 1600 1600 1600 1600 2200 1600 1800 800 800 1200 1200 1600
Electrical Property  
Dielectric Strength kv/mm - 15 15 15 15 15 15 11 13 11 16 14 13 13 -
Dielectric Constant （1MHz）  - - 9.4 9.9 9.9 9.9 9.9 9.9 33 28 11 8.5 8.6 9.6 9.6 -
Dielectric Losses （1MHz） （X10-4） - 4 2 1 1 1 1 16 17 5 2 3 3 3 -
Volume Resistivity 20℃ Ω.cm >1012 >1014 >1014 >1014 >1014 >1014 >1014 1013 >1014 >1013 >1014 >1014 >1014 >1014 108
Volume Resistivity 300℃ Ω.cm - 1010 1010 1013 1013 1013 1013 106 106 1010 1011 1010 1012 1012 -

* This data is an example of test results in lab. It may be different from the actual characteristics in a particular manufacturing process.

  • Density
  • Flexural Strength
  • Compressive Strength
  • Young's Modulus
  • Fracture Toughness
  • Thermal Expansion
  • Thermal Conductivity
  • Specific Heat
  • Max. Service Temp.
  • Dielectric (1MHz)

* This data is an example of test results in lab. It may be different from the actual characteristics in a particular manufacturing process.

REQUEST A QUOTE

Please let us know your product specs and quantity for a quick quote. Submit the form below to get started.

I agree to join the mailing list and receive updates and notifications.

*Please enter your company email address. Responses may be delayed for personal addresses.

※Please ensure you understand our privacy policy before submission.

※Required fields.

2025 ＠ Japan Fine Materials Corporation Privacy Policy

Application form Inquiry phone